HS Code |
262763 |
| Type | E-Glass Direct Roving |
| Material | E-glass continuous filament |
| Filament Diameter | 10-24 microns |
| Tex Range | 200-9600 tex |
| Moisture Content | ≤0.10% |
| Compatability | Thermoset & Thermoplastic resins |
| Tensile Strength | ≥3500 MPa |
| Linear Density Tolerance | ±5% |
| Breaking Tenacity | ≥0.30 N/tex |
| Volatile Content | ≤0.30% |
| Loss On Ignition | 0.40-0.80% |
| Color | White |
| Packaging | Plastic film wrapping, carton or pallet |
| Application | Pultrusion, filament winding, weaving |
As an accredited E-Glass Direct Roving factory, we enforce strict quality protocols—every batch undergoes rigorous testing to ensure consistent efficacy and safety standards.
|
Tensile Strength: E-Glass Direct Roving with high tensile strength (≥ 3200 MPa) is used in wind turbine blade manufacturing, where it ensures structural integrity and resistance to mechanical stress. Filament Diameter: E-Glass Direct Roving with 17μm filament diameter is used in pultrusion profiles, where it provides smooth surface finish and enhanced load distribution. Moisture Content: E-Glass Direct Roving with moisture content ≤ 0.15% is used in automotive composite parts, where it delivers optimal resin impregnation and dimensional stability. Tex Size: E-Glass Direct Roving with 2400 tex is used in pipe and tank filament winding, where it achieves high production speed and uniform wall thickness. Compatibility: E-Glass Direct Roving with epoxy resin compatibility is used in marine laminate fabrication, where it ensures strong adhesion and water resistance. Linear Density: E-Glass Direct Roving with linear density controlled at ±2% is used in woven fabrics for construction, where it promotes consistent performance and reliable fabric uniformity. Loss on Ignition: E-Glass Direct Roving with loss on ignition ≤ 0.40% is used in electrical insulation boards, where it maintains dielectric properties and fire retardancy. Stability Temperature: E-Glass Direct Roving with service stability up to 600°C is used in high-temperature insulation products, where it offers long-term thermal durability. Silane Sizing: E-Glass Direct Roving with advanced silane sizing is used in SMC/BMC processes, where it enhances matrix bonding and mechanical strength. |
| Packing | The E-Glass Direct Roving is packaged in 20 kg rolls, each wrapped in plastic film and packed in sturdy cardboard cartons. |
| Container Loading (20′ FCL) | Container Loading (20′ FCL) for E-Glass Direct Roving: 20,000 kg packed on pallets, securely wrapped, maximizing container space efficiently. |
| Shipping | E-Glass Direct Roving is shipped securely wound on robust bobbins, sealed in protective plastic film to prevent moisture absorption, and packed in sturdy, reinforced cardboard boxes or pallets. Each shipment includes clear labeling for product identification, safe handling instructions, and adheres to international standards to ensure quality during transit. |
| Storage | E-Glass Direct Roving should be stored in a clean, dry, and well-ventilated area at room temperature, away from direct sunlight and sources of moisture. Keep it in its original packaging to prevent contamination and mechanical damage. Avoid stacking excessively to prevent deformation. Ensure the storage area is free from chemicals or materials that could affect the roving’s quality and performance. |
| Shelf Life | E-Glass Direct Roving typically has an indefinite shelf life when stored in a cool, dry place away from direct sunlight. |
Competitive E-Glass Direct Roving prices that fit your budget—flexible terms and customized quotes for every order.
For samples, pricing, or more information, please contact us at +8615365186327 or mail to sales3@ascent-chem.com.
We will respond to you as soon as possible.
Tel: +8615365186327
Email: sales3@ascent-chem.com
Flexible payment, competitive price, premium service - Inquire now!